VPSC Input Deck for Yield surface prediction of Aluminum on rolling
From EVOCD
back to Yield surface prediction of Aluminum on rolling
*Material: Aluminum
cubic crysym
1.0 1.0 1.0 90. 90. 90. unit cell axes and angles
Elastic stiffness (single crystal [MPa]; scaled=0.85xINTERPOLATED)
108.2 61.3 61.3 000.0 000.0 000.0
61.3 108.2 61.3 000.0 000.0 000.0
61.3 61.3 108.2 000.0 000.0 000.0
000.0 000.0 000.0 28.5 000.0 000.0
000.0 000.0 000.0 000.0 28.5 000.0
000.0 000.0 000.0 000.0 000.0 28.5
*Thermal expansion coefficients (single crystal in crystal axis):
10.0e-6 10.0e-6 10.0e-6 0.0e0 0.0e0 0.0e0 "alfacc"
*Info about slip & twinning modes in this file:
2 nmodesx (total # of modes listed in file)
1 nmodes (# of modes to be used in the calculation)
1 mode(i) (label of the modes to be used)
<111>{110} SLIP
1 12 20 1 modex,nsmx,nrsx,iopsysx
0.000 0 0.000 0.000 twshx,isectw,thres1,thres2
3.7 30.0 20.0 0.0 0. 0. tau0,tau1,thet0,thet1 ,hpfac,gndfac
1.0 1.0 hlat(nmodes)
1 1 1 0 1 -1
1 1 1 1 0 -1
1 1 1 1 -1 0
-1 1 1 0 1 -1
-1 1 1 1 0 1
-1 1 1 1 1 0
-1 -1 1 0 1 1
-1 -1 1 1 0 1
-1 -1 1 1 -1 0
1 -1 1 0 1 1
1 -1 1 1 0 -1
1 -1 1 1 1 0
<111>{112} TWIN
2 12 20 0 modex,nsmx,nrsx,iopsysx
0.707 0 0.100 0.500 twshx,isectw,thres1,thres2
1.0 0.0 0.0 0.0 0. 0. tau0,tau1,thet0,thet1 ,hpfac,gndfac
1.0 1.0 hlat(nmodes)
1 1 1 -2 1 1
1 1 1 1 -2 1
1 1 1 1 1 -2
-1 1 1 2 1 1
-1 1 1 -1 -2 1
-1 1 1 -1 1 -2
-1 -1 1 2 -1 1
-1 -1 1 -1 2 1
-1 -1 1 -1 -1 -2
1 -1 1 -2 -1 1
1 -1 1 1 2 1
1 -1 1 1 -1 -2