# # Data set for Damage Model v.1.0 # model_tag= DMG # Fields in the data set # material - Tag for material # G - Shear modulus # Bulk - Bulk modulus # a - Constant to adjust shear modulus due to variation of temperature from initial # b - Constant to adjust bulk modulus due to variation of temperature from initial # Tmelt - Melt temperature (K) # heat - Heat generation term # Kic - Particle fracture toughness # nv - Particle McClintock damage constant # fname - Tag for data set # source - Source of data set # comment - Any other comment on data set # excluded - Is dataset excluded? 0=no, 1=yes # dstype - Experiment type: 1=Tension 2=Compression 3=Torsion 4=Tens+Comp 5=Comp+Tens # units - Stress units: 1=psi 2=Ksi 3=Pa 4=KPa 5=MPa 6=GPa # Tinit - Initial temperature # strain - strain values # stress - stress values # dn - Particle average size # fn - Particles volume fraction # dcs0 - Reference grain size or dendrite cell size # dcs - Grain size or dendrite cell size of experiment sample # r0 - Initial radius of a spherical void # volF - Initial void volume fraction # period - Time period (0=no model) # rate - Strain rate # incr - No. of increments (0=no model) # angle - Bi-axial loading ratio # e_load - Strain level for load change (dstype 4 & 5) # material= AE42 G= 16667 Bulk= 50000 a= 0 b= 0 Tmelt= 950 heat= 0.32 Kic= 1000 nv= 0.3 fname= AE42-50-c source= David Oglesby comment= Strain rate not given excluded= 0 dstype= 1 units= 5 Tinit= 223.15 dn= 0 fn= 0.001 dcs0= 30 dcs= 30 r0= 0 volF= 0 period= 7.71905 rate= 0.01 incr= 100 angle= 0.51 e_load= 0 btype= 0 # Experimental data strain, stress= 0.00126193 5.75508 0.00190259 27.7946 0.00202836 16.3839 0.00223639 37.5917 0.00228273 73.4705 0.00237256 65.32 0.00252528 51.4641 0.00255365 88.973 0.00361794 112.659 0.00377964 97.9882 0.0043664 124.918 0.00506096 142.067 0.00677348 147.024 0.00973894 158.551 0.0127673 164.372 0.0171115 171.058 0.021023 176.913 0.0249436 181.952 0.0279629 188.589 0.0332083 193.678 0.0366693 200.331 0.0419056 206.235 0.047124 213.77 0.0523514 220.489 0.0571282 228.007 0.0606162 232.215 0.0654109 238.102 0.0688899 243.125 0.0737116 246.568 0.0771905 251.591