# Data set for Damage Model v.1.0
#
model_tag= DMG

# Fields in the data set
# material - Tag for material
# G - Shear modulus
# Bulk - Bulk modulus
# a - Constant to adjust shear modulus due to variation of temperature from initial
# b - Constant to adjust bulk modulus due to variation of temperature from initial
# Tmelt - Melt temperature (K)
# heat - Heat generation term
# Kic - Particle fracture toughness
# nv - Particle McClintock damage constant
# fname - Tag for data set
# source - Source of data set
# comment - Any other comment on data set
# excluded - Is dataset excluded? 0=no, 1=yes
# dstype - Experiment type: 1=Tension 2=Compression 3=Torsion 4=Tens+Comp 5=Comp+Tens
# units - Stress units: 1=psi 2=Ksi 3=Pa  4=KPa 5=MPa 6=GPa
# Tinit - Initial temperature
# strain - strain values
# stress - stress values
# dn - Particle average size
# fn - Particles volume fraction
# dcs0 - Reference grain size or dendrite cell size
# dcs - Grain size or dendrite cell size of experiment sample
# r0 - Initial radius of a spherical void
# volF - Initial void volume fraction
# period - Time period (0=no model)
# rate - Strain rate
# incr - No. of increments (0=no model)
# angle - Bi-axial loading ratio
# e_load - Strain level for load change (dstype 4 & 5)
#
material= AE42
G= 16667
Bulk= 50000
a= 0
b= 0
Tmelt= 950
heat= 0.32
Kic= 1000
nv= 0.3
fname= AE42-23c
source= David Oglesby
comment= Strain rate not given
excluded= 0
dstype= 1
units= 5
Tinit= 296.15
dn= 0
fn= 0.001
dcs0= 30
dcs= 30
r0= 0
volF= 0
period= 11.4519
rate= 0.01
incr= 100
angle= 0.51
e_load= 0
btype= 0

# Experimental data
strain, stress=
0.000387704 4.90687
0.0011721 13.9056
0.00179479 37.5751
0.00184112 73.4539
0.00191157 26.9795
0.00196689 62.0432
0.00210164 49.8175
0.00258958 85.7128
0.00288745 98.7701
0.00322125 108.567
0.00354607 119.18
0.00430352 130.623
0.0046463 139.605
0.00856684 144.645
0.0120637 148.038
0.0146774 151.397
0.0181833 153.975
0.0216623 158.998
0.0260334 163.239
0.0299539 168.279
0.0338835 172.503
0.037804 177.543
0.0408503 181.734
0.0447799 185.959
0.049133 191.83
0.0539458 196.087
0.0587405 201.975
0.0631206 205.401
0.0675007 208.827
0.0714482 211.421
0.0771532 214.897
0.0815423 217.508
0.0854987 219.287
0.0889867 223.495
0.094259 226.139
0.0973412 227.071
0.101289 229.665
0.104371 230.596
0.108796 229.947
0.111887 230.063
0.114519 231.792