# Data set for Damage Model v.1.0
#
model_tag= DMG

# Fields in the data set
# material - Tag for material
# G - Shear modulus
# Bulk - Bulk modulus
# a - Constant to adjust shear modulus due to variation of temperature from initial
# b - Constant to adjust bulk modulus due to variation of temperature from initial
# Tmelt - Melt temperature (K)
# heat - Heat generation term
# Kic - Particle fracture toughness
# nv - Particle McClintock damage constant
# fname - Tag for data set
# source - Source of data set
# comment - Any other comment on data set
# excluded - Is dataset excluded? 0=no, 1=yes
# dstype - Experiment type: 1=Tension 2=Compression 3=Torsion 4=Tens+Comp 5=Comp+Tens
# units - Stress units: 1=psi 2=Ksi 3=Pa  4=KPa 5=MPa 6=GPa
# Tinit - Initial temperature
# strain - strain values
# stress - stress values
# dn - Particle average size
# fn - Particles volume fraction
# dcs0 - Reference grain size or dendrite cell size
# dcs - Grain size or dendrite cell size of experiment sample
# r0 - Initial radius of a spherical void
# volF - Initial void volume fraction
# period - Time period (0=no model)
# rate - Strain rate
# incr - No. of increments (0=no model)
# angle - Bi-axial loading ratio
# e_load - Strain level for load change (dstype 4 & 5)
#
material= AZ91
G= 16666.7
Bulk= 50000
a= 0
b= 0
Tmelt= 3000
heat= 0.34
Kic= 1000
nv= 0
fname= AZ91data23c
source= default
comment= default
excluded= 0
dstype= 1
units= 5
Tinit= 296.15
dn= 0
fn= 0.001
dcs0= 30
dcs= 30
r0= 0
volF= 0
period= 7.00238
rate= 0.01
incr= 100
angle= 0.51
e_load= 0
btype= 0

# Experimental data
strain, stress=
0.000392429 4.80341
0.00108031 59.0979
0.00113813 17.601
0.00118798 50.3234
0.00132591 75.8666
0.00142289 31.1789
0.0032489 103.074
0.00342509 88.7161
0.00353366 116.652
0.00562305 130.299
0.00640791 139.906
0.00671224 151.889
0.0074971 161.496
0.0091647 172.733
0.0130881 184.056
0.0166092 191.373
0.0219155 200.356
0.027251 206.945
0.0321453 212.719
0.0379418 218.528
0.0432676 225.915
0.0481618 231.689
0.0517417 234.22
0.0570871 240.012
0.0606376 244.936
0.0642077 248.265
0.0673266 251.577
0.0700238 252.479