# # Data set for Damage Model v.1.0 # model_tag= DMG # Fields in the data set # material - Tag for material # G - Shear modulus # Bulk - Bulk modulus # a - Constant to adjust shear modulus due to variation of temperature from initial # b - Constant to adjust bulk modulus due to variation of temperature from initial # Tmelt - Melt temperature (K) # heat - Heat generation term # Kic - Particle fracture toughness # nv - Particle McClintock damage constant # fname - Tag for data set # source - Source of data set # comment - Any other comment on data set # excluded - Is dataset excluded? 0=no, 1=yes # dstype - Experiment type: 1=Tension 2=Compression 3=Torsion 4=Tens+Comp 5=Comp+Tens # units - Stress units: 1=psi 2=Ksi 3=Pa 4=KPa 5=MPa 6=GPa # Tinit - Initial temperature # strain - strain values # stress - stress values # dn - Particle average size # fn - Particles volume fraction # dcs0 - Reference grain size or dendrite cell size # dcs - Grain size or dendrite cell size of experiment sample # r0 - Initial radius of a spherical void # volF - Initial void volume fraction # period - Time period (0=no model) # rate - Strain rate # incr - No. of increments (0=no model) # angle - Bi-axial loading ratio # e_load - Strain level for load change (dstype 4 & 5) # material= AZ91 G= 16666.7 Bulk= 50000 a= 0 b= 0 Tmelt= 3000 heat= 0.34 Kic= 1000 nv= 0 fname= AZ91data75c source= default comment= default excluded= 0 dstype= 1 units= 5 Tinit= 348.15 dn= 0 fn= 0.001 dcs0= 30 dcs= 30 r0= 0 volF= 0 period= 9.66812 rate= 0.01 incr= 100 angle= 0.51 e_load= 0 btype= 0 # Experimental data strain, stress= 0.000245606 16.7687 0.000353276 7.99415 0.00126628 43.9419 0.00147183 27.1905 0.00185538 69.5024 0.00249251 54.3637 0.00263044 79.9069 0.00290542 94.2825 0.00452407 109.508 0.0052502 123.901 0.00602527 134.305 0.0067514 148.698 0.00752646 159.103 0.00918427 171.137 0.0122249 180.831 0.0175507 188.217 0.0210719 195.535 0.0259759 200.511 0.0308701 206.286 0.0344206 211.21 0.0397758 216.204 0.0428752 221.111 0.0459941 224.423 0.0504861 226.192 0.0553901 231.168 0.0607648 234.566 0.0665907 237.982 0.0719753 240.583 0.0764673 242.351 0.081381 246.53 0.0863438 246.72 0.0904042 246.876 0.0944352 249.425 0.0966812 250.309