# # Data set for Damage Model v.1.0 # model_tag= DMG # Fields in the data set # material - Tag for material # G - Shear modulus # Bulk - Bulk modulus # a - Constant to adjust shear modulus due to variation of temperature from initial # b - Constant to adjust bulk modulus due to variation of temperature from initial # Tmelt - Melt temperature (K) # heat - Heat generation term # Kic - Particle fracture toughness # nv - Particle McClintock damage constant # fname - Tag for data set # source - Source of data set # comment - Any other comment on data set # excluded - Is dataset excluded? 0=no, 1=yes # dstype - Experiment type: 1=Tension 2=Compression 3=Torsion 4=Tens+Comp 5=Comp+Tens # units - Stress units: 1=psi 2=Ksi 3=Pa 4=KPa 5=MPa 6=GPa # Tinit - Initial temperature # strain - strain values # stress - stress values # dn - Particle average size # fn - Particles volume fraction # dcs0 - Reference grain size or dendrite cell size # dcs - Grain size or dendrite cell size of experiment sample # r0 - Initial radius of a spherical void # volF - Initial void volume fraction # period - Time period (0=no model) # rate - Strain rate # incr - No. of increments (0=no model) # angle - Bi-axial loading ratio # e_load - Strain level for load change (dstype 4 & 5) # material= AZ91 G= 16666.7 Bulk= 50000 a= 0 b= 0 Tmelt= 3000 heat= 0.34 Kic= 1000 nv= 0 fname= AZ91data150c source= default comment= default excluded= 0 dstype= 1 units= 5 Tinit= 423.15 dn= 0 fn= 0.001 dcs0= 30 dcs= 30 r0= 0 volF= 0 period= 23.4928 rate= 0.01 incr= 100 angle= 0.51 e_load= 0 btype= 0 # Experimental data strain, stress= 0.000853374 4.02304 0.000981523 30.3639 0.00114792 16.8033 0.00176638 39.9708 0.00232611 67.9243 0.0025023 53.566 0.00307181 80.7219 0.00428825 91.9414 0.00504374 103.941 0.00626018 115.161 0.00793757 125.6 0.0123415 134.548 0.0180988 143.547 0.0225713 146.911 0.0283874 151.124 0.0351547 151.384 0.0419123 152.441 0.049121 153.516 0.0558688 155.371 0.0631069 154.052 0.0712277 154.364 0.0797997 154.693 0.087028 154.172 0.0951587 153.686 0.101946 152.35 0.108262 152.592 0.114588 152.037 0.120031 149.851 0.125896 150.076 0.133154 147.162 0.141284 146.676 0.148964 146.173 0.155309 144.022 0.162077 144.282 0.168864 142.946 0.174748 141.575 0.181967 141.852 0.187861 139.684 0.193285 139.094 0.199621 137.741 0.204142 137.117 0.209154 133.319 0.215009 134.341 0.220442 132.953 0.226327 131.583 0.2313 130.976 0.234928 129.519