# Data set for Damage Model v.1.0
#
model_tag= DMG

# Fields in the data set
# material - Tag for material
# G - Shear modulus
# Bulk - Bulk modulus
# a - Constant to adjust shear modulus due to variation of temperature from initial
# b - Constant to adjust bulk modulus due to variation of temperature from initial
# Tmelt - Melt temperature (K)
# heat - Heat generation term
# Kic - Particle fracture toughness
# nv - Particle McClintock damage constant
# fname - Tag for data set
# source - Source of data set
# comment - Any other comment on data set
# excluded - Is dataset excluded? 0=no, 1=yes
# dstype - Experiment type: 1=Tension 2=Compression 3=Torsion 4=Tens+Comp 5=Comp+Tens
# units - Stress units: 1=psi 2=Ksi 3=Pa  4=KPa 5=MPa 6=GPa
# Tinit - Initial temperature
# strain - strain values
# stress - stress values
# dn - Particle average size
# fn - Particles volume fraction
# dcs0 - Reference grain size or dendrite cell size
# dcs - Grain size or dendrite cell size of experiment sample
# r0 - Initial radius of a spherical void
# volF - Initial void volume fraction
# period - Time period (0=no model)
# rate - Strain rate
# incr - No. of increments (0=no model)
# angle - Bi-axial loading ratio
# e_load - Strain level for load change (dstype 4 & 5)
#
material= AE42
G= 16667
Bulk= 50000
a= 0
b= 0
Tmelt= 950
heat= 0.32
Kic= 1000
nv= 0.3
fname= AE42-75c
source= David Oglesby
comment= Strain rate not given
excluded= 0
dstype= 1
units= 5
Tinit= 348.15
dn= 0
fn= 0.001
dcs0= 30
dcs= 30
r0= 0
volF= 0
period= 14.8666
rate= 0.01
incr= 100
angle= 0.51
e_load= 0
btype= 0

# Experimental data
strain, stress=
0.000423638 1.64668
0.00119905 11.4604
0.00131725 40.8188
0.0013981 33.4833
0.00149692 24.5178
0.00149833 64.4718
0.0015702 57.9514
0.00168699 47.3557
0.00182315 75.084
0.00214797 85.6962
0.0029144 96.325
0.00323922 106.937
0.00359997 114.289
0.00525859 124.136
0.00740373 129.924
0.0104321 135.746
0.0130368 139.92
0.0160831 144.112
0.0191384 147.488
0.0230679 151.713
0.0269885 156.752
0.0304674 161.775
0.0335317 164.336
0.0374433 170.191
0.0413818 173.6
0.0448877 176.178
0.0488262 179.587
0.0527647 182.997
0.0562616 186.39
0.0606417 189.816
0.063697 193.192
0.0680771 196.618
0.0724572 200.044
0.0755395 200.975
0.0790633 201.923
0.0825692 204.5
0.0860841 206.263
0.089599 208.026
0.0926722 209.772
0.0961871 211.535
0.0997109 212.483
0.102352 213.397
0.105866 215.16
0.110283 215.326
0.112923 216.24
0.116447 217.188
0.11998 217.32
0.123945 218.285
0.126586 219.199
0.130119 219.332
0.13321 219.448
0.13586 219.547
0.138951 219.664
0.142042 219.78
0.145133 219.896
0.146891 220.777
0.148666 220.028