# Data set for Damage Model v.1.0
#
model_tag= DMG

# Fields in the data set
# material - Tag for material
# G - Shear modulus
# Bulk - Bulk modulus
# a - Constant to adjust shear modulus due to variation of temperature from initial
# b - Constant to adjust bulk modulus due to variation of temperature from initial
# Tmelt - Melt temperature (K)
# heat - Heat generation term
# Kic - Particle fracture toughness
# nv - Particle McClintock damage constant
# fname - Tag for data set
# source - Source of data set
# comment - Any other comment on data set
# excluded - Is dataset excluded? 0=no, 1=yes
# dstype - Experiment type: 1=Tension 2=Compression 3=Torsion 4=Tens+Comp 5=Comp+Tens
# units - Stress units: 1=psi 2=Ksi 3=Pa  4=KPa 5=MPa 6=GPa
# Tinit - Initial temperature
# strain - strain values
# stress - stress values
# dn - Particle average size
# fn - Particles volume fraction
# dcs0 - Reference grain size or dendrite cell size
# dcs - Grain size or dendrite cell size of experiment sample
# r0 - Initial radius of a spherical void
# volF - Initial void volume fraction
# period - Time period (0=no model)
# rate - Strain rate
# incr - No. of increments (0=no model)
# angle - Bi-axial loading ratio
# e_load - Strain level for load change (dstype 4 & 5)
#
material= AE42
G= 16667
Bulk= 50000
a= 0
b= 0
Tmelt= 950
heat= 0.32
Kic= 1000
nv= 0.3
fname= AE42-100c
source= David Oglesby
comment= Strain rate not given
excluded= 0
dstype= 1
units= 5
Tinit= 373.15
dn= 0
fn= 0.001
dcs0= 30
dcs= 30
r0= 0
volF= 0
period= 16.8267
rate= 0.01
incr= 100
angle= 0.51
e_load= 0
btype= 0

# Experimental data
strain, stress=
0.000423638 1.64668
0.000793375 8.18365
0.00112718 17.9808
0.00203876 55.5228
0.00223639 37.5917
0.00233521 28.6262
0.00256121 48.2039
0.00284111 62.8914
0.00311203 78.3939
0.00317492 72.6886
0.00345482 87.376
0.00372574 102.879
0.00381558 94.728
0.00401463 116.751
0.0040865 110.231
0.00705196 121.757
0.0100983 125.949
0.0131356 130.955
0.0161819 135.146
0.0196609 140.169
0.024023 145.225
0.0283941 149.466
0.0327653 153.707
0.0362442 158.73
0.0410569 162.988
0.0454281 167.229
0.0498082 170.655
0.0550805 173.299
0.0603438 176.758
0.0642733 180.983
0.0682388 181.947
0.0708525 185.307
0.0748 187.901
0.0809645 189.763
0.0862548 190.777
0.0906349 194.203
0.0955015 193.571
0.099449 196.165
0.103414 197.129
0.108254 198.942
0.113103 199.939
0.116636 200.072
0.120601 201.036
0.124576 201.185
0.12855 201.335
0.132515 202.299
0.136021 204.877
0.140446 204.227
0.144421 204.377
0.147512 204.493
0.151045 204.625
0.154569 205.573
0.158093 206.521
0.161643 205.023
0.165627 204.357
0.168267 205.272