# Data set for Damage Model v.1.0
#
model_tag= DMG

# Fields in the data set
# material - Tag for material
# G - Shear modulus
# Bulk - Bulk modulus
# a - Constant to adjust shear modulus due to variation of temperature from initial
# b - Constant to adjust bulk modulus due to variation of temperature from initial
# Tmelt - Melt temperature (K)
# heat - Heat generation term
# Kic - Particle fracture toughness
# nv - Particle McClintock damage constant
# fname - Tag for data set
# source - Source of data set
# comment - Any other comment on data set
# excluded - Is dataset excluded? 0=no, 1=yes
# dstype - Experiment type: 1=Tension 2=Compression 3=Torsion 4=Tens+Comp 5=Comp+Tens
# units - Stress units: 1=psi 2=Ksi 3=Pa  4=KPa 5=MPa 6=GPa
# Tinit - Initial temperature
# strain - strain values
# stress - stress values
# dn - Particle average size
# fn - Particles volume fraction
# dcs0 - Reference grain size or dendrite cell size
# dcs - Grain size or dendrite cell size of experiment sample
# r0 - Initial radius of a spherical void
# volF - Initial void volume fraction
# period - Time period (0=no model)
# rate - Strain rate
# incr - No. of increments (0=no model)
# angle - Bi-axial loading ratio
# e_load - Strain level for load change (dstype 4 & 5)
#
material= AE42
G= 16667
Bulk= 50000
a= 0
b= 0
Tmelt= 950
heat= 0.32
Kic= 1000
nv= 0.3
fname= AE42-20-c
source= David Oglesby
comment= Strain rate not given
excluded= 0
dstype= 1
units= 5
Tinit= 253.15
dn= 0
fn= 0.001
dcs0= 30
dcs= 30
r0= 0
volF= 0
period= 9.0024
rate= 0.01
incr= 100
angle= 0.51
e_load= 0
btype= 0

# Experimental data
strain, stress=
0.000405671 3.27678
0.00108226 22.0561
0.00119905 11.4604
0.00186665 31.0548
0.00239951 62.8748
0.00249833 53.9093
0.00264206 40.8685
0.00303118 85.7293
0.00313899 75.9488
0.00332905 98.7867
0.00409548 109.415
0.00485292 120.859
0.00551155 141.269
0.00561036 132.303
0.00718813 149.486
0.00801744 154.409
0.0114784 161.062
0.0154169 164.471
0.0188779 171.124
0.0228254 173.719
0.0267459 178.758
0.0310811 186.26
0.0354523 190.501
0.040265 194.758
0.043726 201.411
0.0485387 205.669
0.0528739 213.17
0.0568034 217.395
0.0616072 222.467
0.0655187 228.322
0.0707731 232.596
0.0755768 237.669
0.079939 242.725
0.0838775 246.134
0.0873744 249.527
0.090024 249.627