# Data set for Damage Model v.1.0
#
model_tag= DMG

# Fields in the data set
# material - Tag for material
# G - Shear modulus
# Bulk - Bulk modulus
# a - Constant to adjust shear modulus due to variation of temperature from initial
# b - Constant to adjust bulk modulus due to variation of temperature from initial
# Tmelt - Melt temperature (K)
# heat - Heat generation term
# Kic - Particle fracture toughness
# nv - Particle McClintock damage constant
# fname - Tag for data set
# source - Source of data set
# comment - Any other comment on data set
# excluded - Is dataset excluded? 0=no, 1=yes
# dstype - Experiment type: 1=Tension 2=Compression 3=Torsion 4=Tens+Comp 5=Comp+Tens
# units - Stress units: 1=psi 2=Ksi 3=Pa  4=KPa 5=MPa 6=GPa
# Tinit - Initial temperature
# strain - strain values
# stress - stress values
# dn - Particle average size
# fn - Particles volume fraction
# dcs0 - Reference grain size or dendrite cell size
# dcs - Grain size or dendrite cell size of experiment sample
# r0 - Initial radius of a spherical void
# volF - Initial void volume fraction
# period - Time period (0=no model)
# rate - Strain rate
# incr - No. of increments (0=no model)
# angle - Bi-axial loading ratio
# e_load - Strain level for load change (dstype 4 & 5)
#
material= AZ91
G= 16666.7
Bulk= 50000
a= 0
b= 0
Tmelt= 3000
heat= 0.34
Kic= 1000
nv= 0.3
fname= AZ91data125c
source= default
comment= default
excluded= 0
dstype= 1
units= 5
Tinit= 398.15
dn= 1e-006
fn= 0.001
dcs0= 30
dcs= 30
r0= 0
volF= 0
period= 24.2815
rate= 0.01
incr= 100
angle= 0.51
e_load= 0
btype= 0

# Experimental data
strain, stress=
0.000421793 2.41036
0.000755493 11.9999
0.00147183 27.1905
0.00160977 52.7337
0.00177617 39.1731
0.00235547 65.5313
0.00309139 79.1265
0.00409249 107.895
0.0042491 95.1321
0.00483819 120.693
0.00653515 129.536
0.00776138 139.958
0.0107727 152.045
0.014284 160.16
0.0191783 165.934
0.024965 172.541
0.0303202 177.534
0.0383823 182.632
0.0446495 186.863
0.0509461 188.7
0.0567818 191.318
0.0635198 193.971
0.0716407 194.283
0.0801931 196.207
0.0874116 196.484
0.0955226 197.593
0.100937 197.801
0.107253 198.043
0.113128 197.47
0.118532 198.475
0.124838 199.515
0.131605 199.775
0.138373 200.035
0.144248 199.462
0.150564 199.704
0.155075 199.877
0.159136 200.033
0.163647 200.206
0.169983 198.853
0.173592 198.991
0.179457 199.216
0.18443 198.609
0.190776 196.458
0.19617 198.261
0.201594 197.671
0.207027 196.284
0.212029 193.283
0.217904 192.711
0.223347 190.525
0.226956 190.664
0.231487 189.241
0.235116 187.784
0.238755 185.53
0.241462 185.634
0.242815 185.686