# Data set for Damage Model v.1.0
#
model_tag= DMG

# Fields in the data set
# material - Tag for material
# G - Shear modulus
# Bulk - Bulk modulus
# a - Constant to adjust shear modulus due to variation of temperature from initial
# b - Constant to adjust bulk modulus due to variation of temperature from initial
# Tmelt - Melt temperature (K)
# heat - Heat generation term
# Kic - Particle fracture toughness
# nv - Particle McClintock damage constant
# fname - Tag for data set
# source - Source of data set
# comment - Any other comment on data set
# excluded - Is dataset excluded? 0=no, 1=yes
# dstype - Experiment type: 1=Tension 2=Compression 3=Torsion 4=Tens+Comp 5=Comp+Tens
# units - Stress units: 1=psi 2=Ksi 3=Pa  4=KPa 5=MPa 6=GPa
# Tinit - Initial temperature
# strain - strain values
# stress - stress values
# dn - Particle average size
# fn - Particles volume fraction
# dcs0 - Reference grain size or dendrite cell size
# dcs - Grain size or dendrite cell size of experiment sample
# r0 - Initial radius of a spherical void
# volF - Initial void volume fraction
# period - Time period (0=no model)
# rate - Strain rate
# incr - No. of increments (0=no model)
# angle - Bi-axial loading ratio
# e_load - Strain level for load change (dstype 4 & 5)
#
material= etpcu
G= 0
Bulk= 0
a= 0
b= 0
Tmelt= 3000
heat= 0.34
Kic= 1000
nv= 0.3
fname= T1R1P3.A1
source= DR. T. NICHOLAS; MATERIAL BEHAVIOR AT HIGH STRAIN RATES; WRIGHT-PATTERSON AFB, OHIO
comment= STRESS V. STRAIN; FIG. 25
excluded= 0
dstype= 1
units= 5
Tinit= 293
dn= 0
fn= 0.001
dcs0= 30
dcs= 30
r0= 0
volF= 0
period= 0.000220609
rate= 1100
incr= 100
angle= 0.51
e_load= 0
btype= 0

# Experimental data
strain, stress=
4.1771e-006 -0.25119
-0.00028208 16.518
-0.00037779 33.212
-0.00035542 55.335
-0.00069906 79.565
-0.00015255 93.147
0.0010367 106.17
0.0024659 114.54
0.0033731 118.56
0.0053777 123.99
0.0088102 130.17
0.014636 138.73
0.025381 151.84
0.037143 164.49
0.052918 180.19
0.070855 197.44
0.089433 214.2
0.10524 228.38
0.12507 245.54
0.14331 260.68
0.15942 273.18
0.17576 286.12
0.1926 299.5
0.20865 311.57
0.22625 324.73
0.24267 336.99