# # Data set for Damage Model v.1.0 # model_tag= DMG # Fields in the data set # material - Tag for material # G - Shear modulus # Bulk - Bulk modulus # a - Constant to adjust shear modulus due to variation of temperature from initial # b - Constant to adjust bulk modulus due to variation of temperature from initial # Tmelt - Melt temperature (K) # heat - Heat generation term # Kic - Particle fracture toughness # nv - Particle McClintock damage constant # fname - Tag for data set # source - Source of data set # comment - Any other comment on data set # excluded - Is dataset excluded? 0=no, 1=yes # dstype - Experiment type: 1=Tension 2=Compression 3=Torsion 4=Tens+Comp 5=Comp+Tens # units - Stress units: 1=psi 2=Ksi 3=Pa 4=KPa 5=MPa 6=GPa # Tinit - Initial temperature # strain - strain values # stress - stress values # dn - Particle average size # fn - Particles volume fraction # dcs0 - Reference grain size or dendrite cell size # dcs - Grain size or dendrite cell size of experiment sample # r0 - Initial radius of a spherical void # volF - Initial void volume fraction # period - Time period (0=no model) # rate - Strain rate # incr - No. of increments (0=no model) # angle - Bi-axial loading ratio # e_load - Strain level for load change (dstype 4 & 5) # material= AE42 G= 16667 Bulk= 50000 a= 0 b= 0 Tmelt= 950 heat= 0.32 Kic= 1000 nv= 0.3 fname= AE42-150c source= David Oglesby comment= Strain rate not given excluded= 0 dstype= 1 units= 5 Tinit= 423.15 dn= 0 fn= 0.001 dcs0= 30 dcs= 30 r0= 0 volF= 0 period= 23.4272 rate= 0.01 incr= 100 angle= 0.51 e_load= 0 btype= 0 # Experimental data strain, stress= 0.000432621 0.831629 0.000829309 4.92345 0.0016676 9.03186 0.00188462 29.4247 0.00199242 19.6441 0.00205531 13.9387 0.00268698 36.7933 0.00305672 43.3302 0.00324679 66.1682 0.00332764 58.8327 0.00341747 50.6822 0.00347279 85.7459 0.00403118 75.1669 0.0046898 95.5762 0.00776307 97.3224 0.013459 101.613 0.0182538 107.501 0.0235351 109.33 0.029222 114.436 0.034918 118.727 0.0397487 121.354 0.0454626 124.015 0.0502843 127.457 0.0568904 129.336 0.0621537 132.795 0.0665428 135.406 0.0718151 138.05 0.0766548 139.863 0.0823687 142.524 0.0872264 142.706 0.0916155 145.317 0.0964731 145.499 0.102638 147.362 0.108802 149.224 0.115426 149.472 0.121609 149.705 0.127341 150.735 0.133523 150.967 0.138822 151.166 0.14368 151.349 0.149853 152.396 0.155594 152.611 0.160903 151.995 0.167536 151.429 0.17151 151.578 0.175475 152.542 0.180757 154.371 0.186516 152.957 0.19049 153.106 0.19624 152.507 0.201539 152.706 0.205955 152.871 0.210822 152.239 0.216148 149.993 0.220573 149.343 0.224989 149.509 0.228955 150.473 0.231604 150.573 0.234272 149.042