# Data set for Damage Model v.1.0
#
model_tag= DMG

# Fields in the data set
# material - Tag for material
# G - Shear modulus
# Bulk - Bulk modulus
# a - Constant to adjust shear modulus due to variation of temperature from initial
# b - Constant to adjust bulk modulus due to variation of temperature from initial
# Tmelt - Melt temperature (K)
# heat - Heat generation term
# Kic - Particle fracture toughness
# nv - Particle McClintock damage constant
# fname - Tag for data set
# source - Source of data set
# comment - Any other comment on data set
# excluded - Is dataset excluded? 0=no, 1=yes
# dstype - Experiment type: 1=Tension 2=Compression 3=Torsion 4=Tens+Comp 5=Comp+Tens
# units - Stress units: 1=psi 2=Ksi 3=Pa  4=KPa 5=MPa 6=GPa
# Tinit - Initial temperature
# strain - strain values
# stress - stress values
# dn - Particle average size
# fn - Particles volume fraction
# dcs0 - Reference grain size or dendrite cell size
# dcs - Grain size or dendrite cell size of experiment sample
# r0 - Initial radius of a spherical void
# volF - Initial void volume fraction
# period - Time period (0=no model)
# rate - Strain rate
# incr - No. of increments (0=no model)
# angle - Bi-axial loading ratio
# e_load - Strain level for load change (dstype 4 & 5)
#
material= AM50
G= 14740
Bulk= 44220
a= 0
b= 0
Tmelt= 850
heat= 0.5
Kic= 17.3
nv= 0.01
fname= am50data23c.txt
source= <common drive>\Material Database\Magnesium\AM50mag
comment= default
excluded= 0
dstype= 1
units= 5
Tinit= 297
dn= 0.0004
fn= 0.07
dcs0= 20
dcs= 20
r0= 0.0002
volF= 0.112
period= 168
rate= 0.001
incr= 100
angle= 0.51
e_load= 0
btype= 0

# Experimental data
strain, stress=
0.00071048 11.7801
0.00071048 3.14136
0.00106572 67.5393
0.00106572 17.2775
0.00106572 38.4817
0.00106572 27.4869
0.00106572 75.3927
0.00142096 58.1152
0.00142096 85.6021
0.0017762 47.1204
0.00213144 93.4555
0.00248668 100.524
0.00284192 109.162
0.00497336 120.157
0.00639432 125.654
0.00852575 132.723
0.0117229 135.079
0.016341 139.791
0.0198934 143.717
0.0234458 148.429
0.0262877 150.785
0.0291297 153.927
0.0323268 157.853
0.0348135 161.78
0.0390764 164.136
0.0415631 168.848
0.0451155 171.204
0.0479574 172.775
0.051865 177.487
0.0554174 180.628
0.0596803 184.555
0.0639432 186.911
0.0678508 190.838
0.0721137 193.194
0.0753108 196.335
0.0788632 198.691
0.0824156 201.047
0.0856128 202.618
0.0895204 204.974
0.0927176 206.545
0.0969805 208.115
0.0991119 209.686
0.10373 211.257
0.107993 214.398
0.112256 215.969
0.117229 217.539
0.119716 218.325
0.123623 220.681
0.127531 221.466
0.130728 223.037
0.135702 224.607
0.138188 226.178
0.141741 226.963
0.145648 228.534
0.14849 228.534
0.151332 229.319
0.153464 229.319