# # Data set for Damage Model v.1.0 # model_tag= DMG # Fields in the data set # material - Tag for material # G - Shear modulus # Bulk - Bulk modulus # a - Constant to adjust shear modulus due to variation of temperature from initial # b - Constant to adjust bulk modulus due to variation of temperature from initial # Tmelt - Melt temperature (K) # heat - Heat generation term # Kic - Particle fracture toughness # nv - Particle McClintock damage constant # fname - Tag for data set # source - Source of data set # comment - Any other comment on data set # excluded - Is dataset excluded? 0=no, 1=yes # dstype - Experiment type: 1=Tension 2=Compression 3=Torsion 4=Tens+Comp 5=Comp+Tens # units - Stress units: 1=psi 2=Ksi 3=Pa 4=KPa 5=MPa 6=GPa # Tinit - Initial temperature # strain - strain values # stress - stress values # dn - Particle average size # fn - Particles volume fraction # dcs0 - Reference grain size or dendrite cell size # dcs - Grain size or dendrite cell size of experiment sample # r0 - Initial radius of a spherical void # volF - Initial void volume fraction # period - Time period (0=no model) # rate - Strain rate # incr - No. of increments (0=no model) # angle - Bi-axial loading ratio # e_load - Strain level for load change (dstype 4 & 5) # material= AZ91 G= 16666.7 Bulk= 50000 a= 0 b= 0 Tmelt= 3000 heat= 0.34 Kic= 1000 nv= 0.3 fname= AZ91data100c source= default comment= default excluded= 0 dstype= 1 units= 5 Tinit= 373.15 dn= 0 fn= 0.001 dcs0= 30 dcs= 30 r0= 0 volF= 0 period= 13.3911 rate= 0.01 incr= 100 angle= 0.51 e_load= 0 btype= 0 # Experimental data strain, stress= 9.78814e-006 0.797685 0.000726128 14.3929 0.00105004 24.7801 0.00135437 36.7627 0.00195326 61.5256 0.00211966 47.9649 0.00268917 75.1208 0.00344467 87.1207 0.00418058 100.716 0.00494586 111.918 0.00560347 131.895 0.00573072 121.525 0.00595675 139.889 0.00764392 149.53 0.00936046 156.779 0.0115379 163.247 0.0155103 170.582 0.0199142 179.529 0.0270544 186.188 0.0319388 192.76 0.0377451 197.771 0.044444 203.614 0.0516135 207.879 0.0569785 212.075 0.0641579 215.543 0.0695228 219.739 0.0767022 223.207 0.0843621 224.299 0.0902173 225.321 0.096053 227.939 0.100565 228.113 0.10642 229.135 0.112275 230.158 0.117679 231.163 0.121749 230.521 0.127153 231.527 0.130743 233.26 0.133911 232.584