# Data set for Damage Model v.1.0
#
model_tag= DMG

# Fields in the data set
# material - Tag for material
# G - Shear modulus
# Bulk - Bulk modulus
# a - Constant to adjust shear modulus due to variation of temperature from initial
# b - Constant to adjust bulk modulus due to variation of temperature from initial
# Tmelt - Melt temperature (K)
# heat - Heat generation term
# Kic - Particle fracture toughness
# nv - Particle McClintock damage constant
# fname - Tag for data set
# source - Source of data set
# comment - Any other comment on data set
# excluded - Is dataset excluded? 0=no, 1=yes
# dstype - Experiment type: 1=Tension 2=Compression 3=Torsion 4=Tens+Comp 5=Comp+Tens
# units - Stress units: 1=psi 2=Ksi 3=Pa  4=KPa 5=MPa 6=GPa
# Tinit - Initial temperature
# strain - strain values
# stress - stress values
# dn - Particle average size
# fn - Particles volume fraction
# dcs0 - Reference grain size or dendrite cell size
# dcs - Grain size or dendrite cell size of experiment sample
# r0 - Initial radius of a spherical void
# volF - Initial void volume fraction
# period - Time period (0=no model)
# rate - Strain rate
# incr - No. of increments (0=no model)
# angle - Bi-axial loading ratio
# e_load - Strain level for load change (dstype 4 & 5)
#
material= 1100al
G= 0
Bulk= 0
a= 0
b= 0
Tmelt= 3000
heat= 0.34
Kic= 1000
nv= 0.3
fname= T2R4P2.A1
source= HONEYWELL; G.R. JOHNSON AND T.J. HOLMQUIST; TEST DATA AND COMPUTATIONAL STRENGTH AND FRACTURE MODEL CONSTANTS FOR 23 MATERIALS SUBJECTED TO LARGE STRAINS, HIGH STRAIN RATES, AND HIGH TEMPERATURES; SEPTEMBER 1988
comment= TRUE STRESS V. TRUE STRAIN
excluded= 0
dstype= 1
units= 5
Tinit= 472
dn= 0
fn= 0.001
dcs0= 30
dcs= 30
r0= 0
volF= 0
period= 0.000356571
rate= 420
incr= 100
angle= 0.51
e_load= 0
btype= 0

# Experimental data
strain, stress=
0.00012448 0.0015386
1.2636e-005 9.4457
5.6311e-005 19.588
0.00019249 29.902
0.00021867 43.309
0.00041984 53.71
0.00035657 63.592
0.00031333 76.738
0.00046387 87.618
0.00054164 98.112
0.00066359 110.34
0.00050883 119.09
0.010577 120.36
0.024044 121.87
0.034697 122.87
0.047857 124.08
0.061716 124.99
0.074071 125.75
0.086868 126.42
0.098664 126.92
0.11128 127.16
0.12321 127.65
0.13846 128.01
0.14976 128.28