# Data set for Damage Model v.1.0
#
model_tag= DMG

# Fields in the data set
# material - Tag for material
# G - Shear modulus
# Bulk - Bulk modulus
# a - Constant to adjust shear modulus due to variation of temperature from initial
# b - Constant to adjust bulk modulus due to variation of temperature from initial
# Tmelt - Melt temperature (K)
# heat - Heat generation term
# Kic - Particle fracture toughness
# nv - Particle McClintock damage constant
# fname - Tag for data set
# source - Source of data set
# comment - Any other comment on data set
# excluded - Is dataset excluded? 0=no, 1=yes
# dstype - Experiment type: 1=Tension 2=Compression 3=Torsion 4=Tens+Comp 5=Comp+Tens
# units - Stress units: 1=psi 2=Ksi 3=Pa  4=KPa 5=MPa 6=GPa
# Tinit - Initial temperature
# strain - strain values
# stress - stress values
# dn - Particle average size
# fn - Particles volume fraction
# dcs0 - Reference grain size or dendrite cell size
# dcs - Grain size or dendrite cell size of experiment sample
# r0 - Initial radius of a spherical void
# volF - Initial void volume fraction
# period - Time period (0=no model)
# rate - Strain rate
# incr - No. of increments (0=no model)
# angle - Bi-axial loading ratio
# e_load - Strain level for load change (dstype 4 & 5)
#
material= AE42
G= 16667
Bulk= 50000
a= 0
b= 0
Tmelt= 950
heat= 0.32
Kic= 1000
nv= 0.3
fname= AE42-125c
source= David Oglesby
comment= Strain rate not given
excluded= 0
dstype= 1
units= 5
Tinit= 398.15
dn= 0
fn= 0.001
dcs0= 30
dcs= 30
r0= 0
volF= 0
period= 18.1857
rate= 0.01
incr= 100
angle= 0.51
e_load= 0
btype= 0

# Experimental data
strain, stress=
0.000423638 1.64668
0.00159573 15.5522
0.00167658 8.21681
0.00183072 34.3149
0.0019475 23.7193
0.00260613 44.1287
0.00296688 51.4807
0.0032917 62.0929
0.00344584 88.1911
0.00356262 77.5954
0.00365246 69.4449
0.0046898 95.5762
0.00504157 103.743
0.00677206 107.07
0.00890821 113.673
0.0132614 119.544
0.0180651 124.617
0.0237431 130.538
0.0298627 136.475
0.0337832 141.515
0.0386229 143.327
0.0434446 146.77
0.050907 151.127
0.0575041 153.821
0.0640923 157.33
0.0706804 160.839
0.0768359 163.516
0.0838746 166.226
0.0904807 168.105
0.0966363 170.782
0.103251 171.846
0.108974 173.692
0.114265 174.706
0.120438 175.753
0.126611 176.8
0.132803 176.217
0.137661 176.4
0.142951 177.414
0.147817 176.781
0.153558 176.996
0.158858 177.195
0.164166 176.579
0.168582 176.745
0.171673 176.861
0.176098 176.212
0.180091 174.731
0.181857 174.797